Enhancing tribo-mechanical, microstructural morphology, and corrosion performance of AZ91D-magnesium composites through the synergistic reinforcements of silicon nitride and waste glass powder

The present investigation has employed recycled waste glass powder (WGP) and silicon nitride (Si3N4) as reinforcing-agents within AZ91D-matrix composites. The composites were fabricated by employing the vacuum stir casting technique to mitigate the effects of oxidation and to ensure homogeneity, uniformity, and superior wettability among the AZ91D-matrix and reinforcements. A microscopic study provided confirmation of a uniform dispersion of WGP and Si3N4 particles throughout the AZ91D-matrix. The tensile strength of the AZ91D/WGP/Si3N4 composites rise with the inclusion of WGP particulates by up to 1.5 percent in AZ91D/7.5% Si3N4. However, the tensile strength of the AZ91D/9%Si3N4 composite have showed maximum value as compared to other chosen formulations/combinations in the current investigation. The tensile strength of AZ91D/1.5% WGP/7.5% Si3N4 composites has strengthened up to 12.13 percent with the comparison of base alloy AZ91D-matrix. In A1 formulated composite, the amount of WGP particulate has enhanced the hardness of the AZ91D-alloy by up to 1.5 percent. Findings, nevertheless has exhibited that the A6 formulated composite had superior outcomes in terms of hardness. The incorporation of “reinforcing-constituent particulates” with 1.5%WGP + 7.5%Si3N4 combination within the AZ91D-matrix, has further increased fatigue-strength by around 57.84 percent. A weight-loss of 0.312 mg was being unveiled for the A1 formulated fabricated composite. The weight-loss for the A6 formulated fabricated composite, however, was reported to be 0.294 mg. At 5 N loads, 2 m/s sliding speed, and 1000 m of sliding distance, the developed 1.5%WGP/7.5%Si3N4/AZ91D composites was reported to have a rate of wear, and frictional coefficient of 0.0025 mm3/m and 0.315, respectively. The investigation employing scanning electron microscopy (SEM) identified the presence of corrosion pits on the surfaces that had undergone corrosion. These pits were found to be a result of localised surface assaults occurring in corrosive environments. Additionally, SEM pictures of the worn surfaces indicated the emergence of microcracks, which may be associated to the conditions of cyclic loading. Moreover, the tensile-fractography examination for the developed 1.5%WGP/7.5%Si3N4/AZ91D composites has exhibited the brittle fracture failure, including cracks and debonding phenomena. In addition, the EDS spectra-analysis have revealed an apparent existence of the observed Mg-peak, Si-peak, Al-peak, Ca-peak, and O-peak for the 1.5%WGP/7.5%Si3N4/AZ91D composites. Furthermore, the utilisation of X-ray diffraction analysis effectively determined the existence of hard phases inside the AZ91D-matrix, which significantly contributed to the reported enhancement in wear resistance. The development of harder-phases has included, α-Mg, Al12Mg17, SiO2, Si3N4, MgO, and CaO phases within the composite has been accountable for the enhancement of the tribomechanical, and wear-resistance characteristics of the AZ91D/WGP/Si3N4 composites. The Si3N4 has been discovered to have a substantial impact on enhancing mechanical performance and raising the resistance to wear.

The wetting behavior between ceramic particles and magnesium alloy is an important property to consider during casting processes in order to control the flow and distribution of the particles within the magnesium matrix.Ceramic particles, such as SiC, Si 3 N 4, TiB 2 etc. are commonly added to magnesium alloys to improve their mechanical characteristics, including hardness, wear resistance, and thermal stability.However, the effective reinforcement of the ceramic particles within the magnesium matrix depends greatly on their wetting behavior.Wettability between ceramic particles and the magnesium alloy can be affected by several key factors, such as surface energy, interfacial chemistry, and surface roughness.The surface energy of the ceramic particles is generally higher than that of the magnesium alloy, resulting in poor wetting behavior 1 .This can be improved by modifying the surface chemistry of the ceramic particles through chemical treatments or by using surfactants to reduce the surface tension between the ceramic particles and the magnesium alloy.Furthermore, the surface roughness of the ceramic particles and magnesium alloy can also influence their wettability.The presence of rough or uneven surfaces can lead to poor wetting behavior due to the development of a barrier coating between the particles and the alloy.This can be addressed by pre-treatment of the surfaces or by adjusting the casting parameters to ensure a more favorable contact angle.Effective dispersion of ceramic particles within the magnesium alloy is critical for achieving the desired mechanical properties.Therefore, techniques such as ultrasound assisted dispersion, stir casting, and rheo-casting have been developed to improve the wettability of the ceramic particles within the magnesium alloy.Additionally, the use of coupling agents and adhesion promoters can further enhance the interfacial adhesion between ceramic particles and magnesium alloy [2][3][4] .
The investigator must implement his concept in order to use engineering materials.To meet a variety of performance needs, novel materials like composites are currently being developed.The primary driver of the rise of magnesium-based composite materials is the requirement for certain applications for materials with higher elastic modulus, impact endurance, tension strength, and hardness than typical magnesium alloys.The resistance to wear for traditional magnesium alloys is likewise relatively low.Composite construction materials have succeeded in replacing conventional engineering materials 3 .Due to their superior mechanical characteristics, the manufacturing method.All in all, by employing vacuum stir casting for developing composites with enhanced characteristics while minimising the implications concerning oxidation was the intent of this research.
Moreover, the primary focus that is being investigated pertains to the necessity for strengthening the mechanical as well as wear-resistant characteristics of AZ91D magnesium alloy, particularly under circumstances involving cyclic-loading as well as corrosive-surroundings.
As far as research gaps are concerned, the comprehensive analysis on the synergistic influences of WGP and Si 3 N 4 in AZ91D composites is limited in the existing literature.The currently existing knowledge voids pertaining to the inadequate research into microstructural characteristics, the implications of various reinforcing proportions, as well as an in-depth investigation of the mechanisms underlying wear and corrosion resistance for these developed composite materials.
Although the study examines the incorporation of WGP and Si 3 N 4 , there are certain aspects of the existing scholarly scientific literature that have not been thoroughly researched.The reinforcing particulate of magnesiumbased composites have been the focus of prior studies; however, the synergistic impacts of WGP and Si 3 N 4 on AZ91D alloy remained unexplored.Furthermore, there is an absence of studies addressing the impact of these reinforcements on corrosion resistance as well as a thorough investigation of microstructural morphology variations caused by varying compositions.Moreover, the intent for this research being conducted is to address this gap by means of an examination regarding the synergistic combined impacts of all these reinforcement materials on the composites' microstructure morphology, mechanical strength, resistance to wear, and corrosion behaviour.For instance, the interaction-relationship, bonding-strength, wettability, and adhesion-strength of such reinforcing agents with the AZ91D-matrix, the influence of fabrication variables on the physicomechanical characteristics of the composite, and an in-depth comprehension of the tribo-corrosion mechanisms in magnesium-based composites have not been thoroughly explored.
Although prior study has focused on magnesium-based composites, the synergistic impact for recycled WGP as well as silicon nitride on the microstructure morphology, mechanical characteristics, wear resistance, and corrosion behaviour of AZ91D magnesium-based composites remains unresolved.Additional research is required to ascertain the precise contributions of WGP and Si 3 N 4 , as well as how they are distributed as well as the subsequent impacts on numerous characteristics.Prior investigations may have disregarded the necessity of performing a thorough examination of the XRD characteristics of the developed composites as well as the underlying processes that are responsible for the observable enhancements.
In accordance with research goals are concerned, following are the intended objectives, firstly, the intent is to optimise the proportion of weight of WGP and Si 3 N 4 in order to attain enhanced mechanical and wear characteristics of the composite.Secondly, by utilising SEM analysis as well as optical microscopy for examining the distribution of WGP and Si 3 N 4 reinforcing-particulates within the AZ91D-matrix for the intent of microstructural analysis.Comprehend the parameters that are influencing the dispersion.Thirdly, to conduct an assessment concerning the fatigue strength, modulus, ductility, tensile strength, as well as hardness of the composites that have been developed.Determine the optimal WGP as well as Si 3 N 4 blend combination as reinforcing-particulates for strengthening the mechanical characteristics.Then to evaluate the composites' resistance to corrosion in a corrosive environment comprising 3.5% NaCl.Analyse the interaction-correlation among the formation of corrosion-pits, as well as the existence of WGP and Si 3 N 4 reinforcing-particulates.Afterwards, to employ Pinon-Disc testing for evaluating the wear-rates, and coefficient of friction characteristics of the distinct composite formulations to determine the optimal blend combination of reinforcements.Analyse the implications of WGP and Si 3 N 4 reinforcing-particulates on the enhancement of resistance to wear.Finally, to determine the phases contained (α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, CaO) and ascertain how they contributed to the enhanced characteristics through analysing the XRD structure patterns of the composites.
All in all, the investigation seeks to examine the implications of WGP and Si 3 N 4 on AZ91D magnesium-based composites pertaining to their microstructure, physicomechanical characteristics, wear resistance, and corrosion behaviour.The specific aims comprise the following aspects: accomplishing or attaining an even homogenous distribution of reinforcing-agents, determining the mechanical characteristics, exploring the resistance of the developed composites against corrosion, and comprehending their worn behaviour characteristics.
Concerning the scope and significance of the present study, the scope of this research has entailed the development for composites comprising various proportions of WGP and Si3N4, as well as an in-depth analysis of their microstructure morphology, and characteristics.The prospective enhancement for the performance functioning, effectiveness, or efficiency for AZ91D magnesium alloys is of profound paramount significance as it allows or facilitates the possible expansion of their potential applications in industries requiring superior mechanical and corrosion characteristics.The composites' prospective applications in sectors including aviation along with automobiles, that require lightweight materials with remarkable mechanical as well as wear characteristics, are of considerable importance.
Additionally, the aim of the research comprises the manufacturing of advanced AZ91D composites that possess customised characteristics, with the intention of employing them for sectors requiring composites with superior high strength performance.
Moreover, in terms of scientific originality, this research's novelty is derived from its investigation into the implications of combining WGP and Si 3 N 4 as reinforcing constituent particulates on the microstructural morphology, and characteristics of AZ91D composites.A novel aspect has been incorporated to the current scientific literature on magnesium composites resulting from the synergistic blend combinated effect of these materials, their evenly homogenous arranged, and uniformity of distribution within the AZ91D-matrix, along with assessing their implications on mechanical and wear characteristics.Furthermore, the research offers a substantial valuable contribution to the scholarly literature pertaining to corrosion as well as wear processes in magnesium-based composites.In reference to the scientific uniqueness, the unique distinctive characteristic lays in the blend combination of Si 3 N 4 , noted due to its thermodynamic stability, and WGP, a recycled material.The novel employment of these materials simultaneously in magnesium composites enhances insight pertaining their combined synergistic effects on the characteristics of the composite.The comprehensive examination regarding the manufacturing technique, microstructural morphological analysis, and the utilisation of Si3N4 as a reinforcing agent comprise the novel aspects.Additionally, the distinctive uniqueness of this research is the utilisation of SEM analysis to explore wear behaviour as well as evaluate the interfacial adhesion, and bonding-strength of reinforcing particulates.Moreover, to validate the reliability and precision of the findings, this study employed rigorous scientific techniques, including XRD analysis, mechanical testing, microscopic examination, and tribo-corrosion evaluation.Aiding to the rigorousness of this research, Optical Microscopy, SEM, and XRD analysis have been employed to conduct an in-depth assessment of the microstructure morphology, as well as phases that have been formed.
Finally, as far as the practical implications are concerned, the study's findings have substantial implications in practice for sectors that rely on lightweight materials that exhibit enhanced mechanical and wear characteristics.The enhanced tensile strength, hardness, and abrasion resistance of the developed composites could potentially make them valuable for the manufacture of automobile as well as aircraft components, as well as additional structural components where these characteristics are critical.Furthermore, having insight into the material's selection procedure for environments that are corrosive is a real world application-oriented advantageous effects of understanding of corrosion behaviour.The outcomes outline a scientific foundation for the prospective utilisation of Si 3 N 4 as well as recycled WGP throughout the fabrication of advanced magnesium composites that have practical significance across numerous sectors.The practical implications for the developed composites entail the potential of employing them in real-world circumstances that require enhanced resistance to corrosion, wear, as well as mechanical strength.The findings from this investigation might yield valuable insights for industries that make use of magnesium-based alloys, whereas additionally offering direction for future research and development in the field of composite materials.
Furthermore, the incorporation of recycled WGP into the manufacturing of materials conforms with sustainable principles, environmentally friendly practices/standards, and makes a contribution to broader global environmental concern.
According to a thorough assessment of the literature, AZ91D has been used extensively in the development of MMCs and hybrid composites with typical ceramic reinforcing particles.However, only a small amount of research has been done employing "silicon nitride", and "waste glass powder" (WGP) as reinforcement in the AZ91D-matrix.This feature is taken into consideration in the current research, which aims to build an AZ91Dbased composite using silicon nitride as reinforcement.The inclusion of WGP and silicon nitride as "reinforcing particulate constituents" in the AZ91D-matrix material was identified by employing microstructural morphology, wettability, mechanical characteristics, corrosion, tribological, wettability, and XRD investigations.

Matrix material
The matrix-material employed in this work is AZ91D-alloy (Fig. 1) with percent-elemental constituents as exhibited in Table 1.A high-purity-alloy with superior strength, great castability, and exceptional resistant to corrosion is AZ91D-Mg casted-alloy.It is mainly utilised in die-casting alloy.In order to strengthen the physicomechanical  www.nature.com/scientificreports/as well as wear characteristics for the composites, the reinforcement particulates have been incorporated to the matrix material, which functions as the base-material.AZ91D Mg-matrix is well-known for its superior resistance to corrosion, strength, durability, resilience, stability, toughness, and castability.Automobile components, aviation structures, and light-weight applications where the blend combination of minimal density as well as considerable excellent strength is crucial render significant widespread utilisation of AZ91D Mg-cast alloy.
The grain-structure of α-Mg is discernible through microscopic examination, and variations in granular-size and shape could potentially reveal distinctive solidification circumstances or subsequent post-processing techniques.In addition, numerous items, including those for automobiles, household appliances, mobile phones, computers, sports equipment, handheld instruments, housings, and coverings, employ the AZ91D magnesium cast alloy based on the myriads of characteristics as illustrated in Table 2.The optical microscopic pictures of the "AZ91D-Mg casted-alloy" despite the incorporation of reinforcing particulates has been exhibited in Fig. 2. AZ91D magnesium cast alloy optical microscopic images allow one to see the α-Mg grain structure.Depending on how the grains are oriented in relation to the incident light, the boundaries among individual α-Mg grains can be bright or dark.These boundaries serve as a virtuous indication of the α-Mg grain structure.The separation among grain boundaries in the optical images can be employed to compute the size of the α-Mg grains.There will be lesser grain boundaries around regions with larger grains.Variations in grain size and shape may signify to various solidification circumstances or post-processing measures.
From the Fig. 3, the XRD pattern for AZ91D Magnesium cast-alloy has comprised of Mg, Al, and Zn, phases.The AZ91D-alloy has primarily comprised of alpha Mg-phase.Alpha Mg-phase is possessing the hexagonally close-packed crystal-structure.This phase has served as a pivotal role in escalating the alloy's formability as well as ductility characteristics.The second phase is, Beta (β) Phase (Mg 17 Al 12 ), as within the alloy, there is an aluminum-rich phase.This phase is having an orthorhombic crystal-structure.This phase has strengthened the alloy's hardness, strength, and furthermore enhances its durability.The third detected phase is, Gamma (γ) Phase (MgZn 2 ) as this phase has comprised of a significant amount of zinc.Here, the crystal-structure is cubic.This phase has contributed to the enhancement of the creep-resistance of the alloy or alloy's resistant to creep-deformation.The degree to which the structure of a material is orderly-structured in a repeating threedimensional pattern is referred to as its crystallinity.XRD has been employed for AZ91D-alloy to determine the specific crystal-arrangements, structures of crystals, and crystalline-patterns which are related to every phase.The degree of crystallinity serves as an indicator of the material's degree of crystal structure 12,13 .Higher percentages of crystallinity reveal an additional orderly arranged atomic structure 14 .An XRD analysis of AZ91D-alloy can reveal how crystalline it is.This enhanced absorbing-intensity at a specific two-theta angle has indicated a higherpercentage of the corresponding planes of crystallography.Crystallinity variances in AZ91D-alloy may be caused by variables including casting-circumstances and thermal-processing.The measurement for crystallinity might be supported by XRD analysis of the intensity of diffraction patterns peaks.By identifying particular phases and analysing their corresponding concentrations that require absorption intensity at two theta angles.By employing the characteristic locations, orientations, and intensities of the diffraction peak patterns for every phase, it is possible to ascertain the phases that have been identified in the alloy as well as their corresponding proportions.

Reinforcements: primary reinforcement material
Locally available WGP as portrayed in Fig. 4a,b was collected or extracted, rinsed, crushed or pulverized, and milled for ten minutes utilising small-milling machine.WGP particulates with 25 µm in avg.particle-size have been employed as a reinforcing-particulate constituents that have contributed to the development of sustainable composites as illustrated in the Fig. 5. the chemical-constituents have been elucidated in Table 3.Three natural materials-limestone, soda ash, and silica sand-have been employed to make glass-bottles.The components for the glass-bottles are combined with recycled-glass, or "cullet." Glass bottles' main ingredient is "cullet".The "cullet" is also mixed with trace amounts of "magnesium", "Sulphur trioxide", "barium oxide", "ferric oxide", and "aluminium oxide".Colors in the bottles can be accomplished through the addition of several materials; including translucent white glass (through the use of incorporating phosphates, fluorides, Ca, ZnO, and tin), a yellowish-green colour (using chromium oxide), Green (using Cu, Cr, Fe), blue-greens (Co, Cr), Blue (cobalt oxide, Cu), Purples and reds (nickel oxide, Mn), Black (Cu, C, magnesia, Fe). Figure 4a,b has displayed the photograph of "waste glass", and "waste glass powder".The characteristics and for WGP has contributed to resistance to wear, the inclusion of WGP particulates has influenced by strengthening the fracture-toughness thereby enhancing the resistance to crack-initiation as well as crack-propagation.The utilisation of WGP as recycled materials has contributed to an economical viable way, and sustainable manner.WGP has been incorporated into construction materials such as concrete building materials to enhance their resilience, resistance to cracking or damage, toughness, long-lasting viability or reliability, durability and strength.WGP particulates have been employed in composites for a broad spectrum of applications, this material offers an ecologically viable and environmentally-sustainable replacement for conventional reinforcing-particulates 15 .In addition, WGP has been utilised in the development of insulating

Reinforcements: secondary reinforcement material
Silicon Nitride (Si 3 N 4 ) powder is a compound that has been constituted of the elements, silicon and nitrogen as depicted in the Fig. 7. Si 3 N 4 with an avg.particle-size of 20 µm is a superior thermodynamically recognised material in powdered form as exhibited in the Fig. 8. Therefore, Si 3 N 4 powder is the most demanding commercial powder.Si 3 N 4 has facilitated or aided to a strengthening of mechanical characteristics and the enhancement of resistance to wear within the composite.In particle form, Si 3 N 4 reinforcing-constituents have exhibited  www.nature.com/scientificreports/thermodynamic stability.Cutting tools have commonly utilised the Si 3 N 4 as a result of its superior hardness as well as resistance to wear.Si 3 N 4 reinforcing-constituents have been employed in ball bearings to mitigate wear, and strengthen long-lasting viability, reliability, performance functionality, and durability 16,17 .Si 3 N 4 reinforcingconstituents have been utilised in high-temperature parts, including furnace-parts.A broader-spectrum for crystalline-phases for Si 3 N 4 have been identified, including beta-Si 3 N 4 , alpha-Si 3 N 4 , and hexagonal Si 3 N 4 (h-Si 3 N 4 ).
The XRD examination has illustrated that the resulting crystal's lattice-structure is hexagonal in shape.Though, Si 3 N 4 contamination by silicates and iron took place due to the use of low-purity raw silicon.Application of Si 3 N 4 particulates can be observed in various fabrication parts such as Solar cells, integrated circuits, insulators, cutting tools, Medical devices, High-temperature material, Bearings, exhaust gas control valves, rocker arm pads, sparkignition engines, turbochargers, glow-plugs, etc. Figure 7 shows the photograph of Si 3 N 4 powder.Powder XRD of Si 3 N 4 Powder shows 99% purity used in the present study (Fig. 9).Alpha-Si 3 N 4 , beta-Si 3 N 4 , and hexagonal Si 3 N 4 (h-Si 3 N 4 ) are some of the various crystalline phases of Si 3 N 4 .The specific phase(s) present in the sample can be determined by apparently observing for distinct diffraction peaks in the pattern at particular angles (2θ values).Due to each phase's distinct crystal lattice structure, it has displayed a distinct pattern.Amorphous or less crystalline Si 3 N 4 phases have exhibited broad, diffuse peaks, while highly crystalline Si 3 N 4 phases have displayed sharp, well-defined peaks.By contrasting peak intensities and shapes with reference patterns, it is possible to determine the level of crystallinity.A higher level of crystallinity implies that a greater proportion of the sample has undergone crystalline structure transformation.Additionally, it can be inferred from the XRD pattern that the hexagonal Si 3 N 4 phase (h-Si 3 N 4 ) has a distinctive hexagonal crystal lattice structure.It is possible that a sizeable portion of the Si 3 N 4 powder has changed into crystalline phases because sharp, well-defined peaks suggest a high degree of crystallinity.Broad peaks might be an indication of amorphous or less crystalline regions.A deeper comprehension of the properties of the material is made possible by the determination of the crystal-structure, which offers intuitions into the arrangement of silicon and nitrogen atoms within the lattice of the identified Si 3 N 4 phases.

Development of composites using vacuum stir casting
The composite was formed using an adaptation of the stir-casting procedure (Fig. 10a,b).The electric furnace heated the magnesium alloy to a temperature of around 680 °C.Additionally, while adding the reinforcement particle combinations to the molten matrix material, WGP and Si 3 N 4 particulates have been heated.During the casting-method, the mould was 300 °C preheated.The parameter's during processing has been depicted in Table 4.The "preheated reinforcing particulates" have been introduced to the matrix-material in accordance with the proportions stated in Table 5 once the magnesium alloy has completely melted (680 °C).The vertex was produced by employing a stirrer, while the AZ91D-matrix was further strengthened with pre-heated reinforcingparticulates utilising a hopper in compliance with the formulations as listed in Table 5.In a graphite-crucible, the AZ91D-matrix and reinforcing-particulates have been blended.The homogeneity or uniformity-dispersion of the blend-combination have been attained through the agitating process, which facilitated or allowed or aided an even-distribution for the reinforcing material within the AZ91D-matrix.In order to prevent the exposure of air's  www.nature.com/scientificreports/contact to the molten magnesium alloy, a vacuum pump as well as a vacuum glass cover box were employed 18,19 .With a vacuum pump's calibrated to approximately 50 mbar, a super-vacuum was developed within the vacuum glass cover-box.An agitator constructed of mild steel was employed in this research to agitate the composite material.A stainless-steel agitator has been utilised in order to avert any potential contamination.Uniformly consistent rate of stirring or speed of agitation and duration have been employed throughout the preparation of each sample.A 125 rpm of stirring-speed, and 5 min of stirring-duration have been maintained throughout the processing of every sample.The agitator has been removed once the composite has reached the mushystage condition.Additionally, a Mg-based composite blend-combination in the mushy-zone was being poured within vacuum environmental conditions to greyish cast-iron moulds.The casting-mould was being encased or enclosed in an enclosed or sealed vacuum-box.Additionally, Zircon/Water-based shield barrier coating-layers has been applied to the casting-mould with the aim to avoid the formation of pore-cracks, fractures, as well as ruptures inside the composite throughout the process of separation of casted specimen's subsequent solidification.Following this, the resulting blend is then poured into an appropriate mould and then allowed to solidify.After the composite material has cooled down, it gets removed from the mould, allowed to air-dry, and then undergoes finishing processing operations in order to achieve the desired shape and dimensions as exhibited in the Fig. 11.In addition, various casting parameters have influenced the mechanical characteristics of the composite such as stirring-speed, stirring-time, wt% of reinforcement, pre-heat temperature of reinforcement, and stirrer material.To keep the molten Mg-alloy from coming in contact with the air, a vacuum-pump and vacuum-box were being employed as discussed in the former statements.In this investigation, the AZ91D-based composite was blended utilising stainless steel as a stirrer material.To develop every specimen, the stirring duration and speed were maintained consistent.For the growth of every respective fabricated composite specimen's, the "stirringspeed", and "duration" were maintained at 125 rpm and 5 min, respectively.The stirrer was taken out once the composite material had become mushy.
Testing for the developed Si 3 N 4 /WGP/AZ91D Mg-MMCs composites The mechanical tests were conducted employing a Vickers-hardness testing for the measurement of hardness test and a Universal testing machine (UTM) for tensile testing.Calibration of UTM has been conducted to assure reliable, precise and accurate outcomes in mechanical examinations.The process entailed confirming, validating the functionality performance, and capability for the displacement-transducer, assuring that the load-cell as well as specimen have been positioned correctly, accurately oriented, properly aligned, and affirming the degree of precision of the forces measurement system.The tensile load is applied to a specimen clamped between two holders up until it fractures throughout the tensile examination by utilising the ASTM E8/E8M as exhibited in the Fig. 12a.The characteristics including the "ultimate tensile strength", "yield strength", and "elongation" have been assessed by this method of testing.The calibration method for the hardness-test apparatus was performed in a comparable manner.In order to properly calibrate a hardness measuring apparatus, its readings have been compared to a standard-reference and the machine was adjusted as required by utilising the ASTM-E18 standard.Samples for the fatigue-test have been prepared in compliance with the ASTM-E606 standard.Both optical microscopy as well as SEM analysis have been employed to examine the metallic characterization of the developed AZ91D Mg-MMCs as illustrated in the Fig. 12b.SEM analysis has been employed for higher-resolution imaging.
In this study, "secondary electron" (SE), as well as "back-scattered electron" (BSE) detectors have been employed for compositional contrast as well as surface imaging, respectively.A motorized-stage is employed to attain accurate sample-orientation, placement, and positioning.To mitigate electron scattering, a vacuum-environment was being employed within the chamber.In contrast, micro structure test has entailed a microscopic examination of the material's structure, facilitating the identification of imperfections as well as abnormalities or inconsistencies or irregularities that may have noticeable implications on its functional and operational characteristics.The samples of metallography have been developed in conformity with the ASTM-E3-95 standard.In order to evaluate the microstructure of the specimens, their surfaces were polished as well as etched with Keller's reagent (10 ml HF + 50 ml H 2 O + 15 ml Hcl + 25 ml HNO 3 ).This etchant is effective in revealing microstructural details and enhancing the contrast between different phases, allowing for a detailed examination of the sample's surface morphology.SEM analysis has been employed for assessing the wear-pattern phenomenon, and worn-out surface characteristics for the composite samples with deteriorated surfaces.For the identification of phase-analysis, a "powdered X-ray diffractometer" was being employed.A mono-chromatic, higher-intensity X-ray source, like, "Cu Kα-radiation".A sensitive, higher-resolution equipment, such as a "scintillation detector".A "motorizedgoniometer" is being utilised to ensure accurate sample positioning and orientation.A sample-holder is an apparatus designed for holding casted composite-specimens and facilitates rotation.The diffraction-patterns and outcomes reported below conclusively indicate the existence of reinforcement-particulates throughout the AZ91D-matrix alloy, even though in distinct or varying concentrations/proportions.

Wear testing evaluation
Cylindrical-pins (AZ91D-based Mg-composites comprised of distinct formulated compositions of WGP and Si 3 N 4 particulates) measuring 6 mm in diameter as well as 10 mm in height have been employed throughout the Pin on Disc investigation trial-testing employing ASTM-G65 standard.The diameter as well as thickness of the (235-HV10 hardness) cast-iron discs have been 63 mm as well as 6 mm, respectively.Among the disc and pin, a thick layer of solid-lubricants has been applied to simulate the actual realistic operational circumstances.The choice of pin on disc specifications has been determined by the findings of the pilot-test that was performed.The frictional, and wear characteristics of Mg-based composites comprising various blend-combinations of Si 3 N 4 as well as WGP reinforcing-particulates have been reported at 5N loads, sliding-speed of 2 m/s, and a sliding-distance of 1000 m.In order to evaluate the tribological characteristics of the material, the coefficient of friction was being observed, measured, and recorded throughout the experiments.SEM analysis has been employed for assessing the wear-pattern phenomenon, and worn-out surface characteristics for the composite samples with deteriorated surfaces.

Corrosion testing
The corrosion performance or activity of AZ91D-based Mg-composite samples with WGP and Si 3 N 4 reinforcingparticulates involves immersion in a 3.5 wt% NaCl corrosive-media solution for 120 h as portrayed in the Fig. 13.
The experimental method has included an assessing corrosion-resistance, measuring of weight-loss, and analyzing the surface-morphology.This method has aided in examining the protective efficacy of diverse multifaceted composites against corrosive environments.SEM analysis has been employed for assessing the corroded-surface phenomenon, pits, and corrosion-products for the composite samples.

Rationale behind the selection of proposed material combination with wt. percent of the reinforcing-particulates for AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites with scientific mechanism
From the in-depth literature scholarly analysis, the rationale motivation for examining the selected formulated composition of the proposed composites formulation have been elucidated based upon the following considerations [20][21][22][23][24] .

Waste glass powder (WGP)
The analysis substantiated that the WGP particulates have been homogenously-dispersed or evenly-distributed across the AZ91D matrix, revealing that the blending process was efficient.The incorporation of 1.5% WGP by weight has strengthened the material's mechanical characteristics considerably.

Si 3 N 4 (Silicon Nitride)
Si 3 N 4 particulates have exhibited a comparable type or degree of a homogenously-dispersion within the AZ91D matrix as that of or likewise the WGP particulate.The incorporation of Si 3 N 4 at a wt% of 7.5% has contributed to or yielded a substantial rise in resistance to wear.

Synergistic combined implications for WGP and Si 3 N 4 particulates
The findings for the research have reported that the incorporation of 1.5% WGP and 7.5% Si 3 N 4 has culminated to a significant enhancement in resistance to wear, physicomechanical characteristics in accordance with the principles of sustainability.Also, the XRD analysis was employed for confirming the existence of harder phases within the AZ91D matrix, which were identified as the primary contributing factors for the reported enhancement of resistance to wear.Now, the analysis for the proposed developed composite material formulation, which incorporates Si 3 N 4 and WGP as reinforcing agents in AZ91D magnesium-based composites, is based on a broader-array of factor considerations designed to strengthen the material's mechanical as well as wear-resistant characteristics.The wt% of reinforcing-particulates selected are 7.5 percent for Si 3 N 4 and 1.5 percent for WGP.
Outlined below are the underlyiing principles with key fundamental concepts which underlay this composition as well as the possible upsides that it could offer:

Microscopy analysis to ascertain homogeneous distribution
The optimum wt% formulated composition of 1.5% WGP and 7.5% Si 3 N 4 reinforcing-particulates were evidently selected with the objective to accomplish an even homogeneous-distribution while retaining the AZ91D Mg-matrix's integrity.The selected optimal wt% formulated composition for reinforcing enhanced www.nature.com/scientificreports/interfacial-adhesion, and bond-strength, thus enhancing wettability characteristics.In accordance with the findings of microstructure analysis, WGP and Si 3 N 4 particulates have been evenly dispersed throughout the AZ91D matrix, and wettability analysis have revealed the resilient interface-adhesion, durable interaction adherence, robust bonding-strength among the WGP as well as Si 3 N 4 reinforcing-particulates and AZ91D-Mg matrix.Achieving this uniformity of distribution or even-dispersion has been accomplished by employing suitable techniques such as efficient melt-processing as well as agitation by the mechanical means.In addition, the underlying key objective is to attain an evenly homogeneous-distribution of WGP and Si 3 N 4 across the AZ91D matrix.This has been affirmed by a microscopic analysis, which confirms that the reinforcing-particulates were dispersed uniformly throughout the AZ91D-matrix during the manufacturing technique.Ensuring this evenly uniformly distribution is of paramount significance in accomplishing strengthened material characteristics, as it promises a consistent homogenous-dispersion of reinforcements, which eventually makes a contribution to strengthened mechanical as well as wear characteristics.

Enhancements of mechanical characteristics
In order to optimally utilise or maximise the reinforcement's implications for mechanical characteristics, including hardness and tensile strength, the precise wt% of formulated composition of 1.5% WGP and 7.5% Si 3 N 4 have been chosen.The incorporation of Si 3 N 4 exhibited significant implications on the enhancement of mechanical efficiency, effectiveness, and performance functioning.The fatigue strength, ductility, tensile strength, and hardness of the developed composites have been evaluated.The findings confirm that the selected formulation, comprised of 1.5% WGP and 7.5% Si 3 N 4 , reveals strengthened mechanical characteristics.The material's mechanical characteristics are considerably enhanced through the incorporation of 1.5% WGP and 7.5% Si 3 N 4 .The composite's enhanced work-hardening as well as tensile strength seemed illustrative evidence of the beneficial constructive or favorable influence that the reinforcement had on the composite's mechanical characteristics.
Additionally, it has been reported that this particular combination of factors raises tensile strength, hardness, and fatigue strength, revealing that the wt% outlined above played a significant indispensable role in strengthening the mechanical characteristics of the composite.

Enhancement of resistance to wear
The research emphasises on the enhancement of resistance to wear, and it has been unveiled that the synergistic combined-blend effect of 1.5% WGP and 7.5% Si 3 N 4 yields a substantial improvement in this context.The wear-rate and coefficient of friction for the composite have been considerably reduced, in particular when the blend combination formulated composition of 1.5% WGP and 7.5% Si 3 N 4 as reinforcing-particulate constituents was being utilised.Moreover, regarding applications where the material will be exposed both to friction and abrasive-wear, such as automotive or industrial components, this is of paramount significance.In addition, the strengthening of the wear-resistance is of crucial significance in applications that has subjected the developed composites to abrasive circumstances, as it effectively prolongs its functional service performance, longevity, durability, and operational lifespan.

Structural analysis
The existence of harder ceramic refractory-phases within the AZ91D matrix, including α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, and CaO, can be identified through XRD analysis.Raised resistance to wear has been attributed to the existence of these phases.The selected wt% of reinforcements have facilitated/aided in the development of these harder ceramic refractory phases, which strengthen the composite against deformation, wear, degradation, deterioration and corrosion.

Corrosion performance and mechanisms
The resistance to corrosion has been strengthened by the protective oxide shield layer or barrier on AZ91D Mg-matrix, and by the inclusion of silicon dioxide (SiO 2 ) in WGP particulates.In addition, within a NaCl solution, the corrosion performance for the composites has been explored.The corrosion resistance of a material can be ascertained through weight loss measurements, while SEM images offer significant insights and valuable perspectives towards the development of corrosion-pits.Hence, the choice for the proposed composite material composition-consisting of 7.5% Si 3 N 4 and 1.5% WGP-is based on its capacity to aid in an evenly-dispersed, uniformly consistent distribution of reinforcingparticulates, enhanced physico-mechanical characteristics, strengthen resistance to wear, and reveal optimal desirable and promising performance during tribological and corrosion assessments.The extensive experimental as well as analytical methodology yields an in-depth analysis of the material's functionality, performance effectiveness or capabilities, and ability to be utilised as a novel and enhanced substitution or replacement.

Microstructure analysis and wettability analysis for the representative samples
The developed AZ91D-based composites reinforced by employing WGP, and Si 3 N 4 has been depicted in Fig. 14a-c using SEM images.The nearly consistent-separation of the WGP, and Si 3 N 4 in AZ91D + 1.5%WGP + 7.5% Si 3 N 4 composites is visible in the microstructures.For all compositions, equitable distribution can be seen though.
For composition A1, within the AZ91D matrix, the SEM images of this composition has revealed a nearly persistent division of waste-glass powder and Si 3 N 4 .The WGP and Si 3 N 4 particles can be observe to be evenly distributed throughout the matrix owing to the analysis of its microstructure.This suggests that these additives are distributed within the AZ91D alloy fairly uniformly 20,21  The fabrication process's appropriate mixing, the additives' adequate distribution in the alloy melt, and perhaps interactions among the additives and the AZ91D matrix that stimulate even distribution are all factors that can be linked to the mechanism causing this distribution.
For composition A6, the SEM images has revealed a microstructure primarily constituted of the Si 3 N 4 additive.Despite the absence of WGP particulate, it is anticipated that the Si 3 N 4 particles will be distributed throughout the AZ91D matrix, possibly resulting in a distinct morphology from the original composition 22,23 .Si 3 N 4 distribution may be influenced by manufacturing-related variables like the melting and mixing conditions.
For composition A7, SEM images of this composition has unveiled a microstructure primarily composed up of the WGP particulate within the AZ91D matrix.The powder particles of waste glass are probably scattered throughout the matrix.Once more, factors like melting and blending during fabrication could have an impact on the distribution.
Additionally, the fair-distribution of additives across all compositions, as observe in the SEM images, implies that the fabrication process was effective in achieving a comparatively homogenously-distribution of the WGP and Si 3 N 4 within the AZ91D matrix 24 .This equitable distribution is influenced by a number of factors: (1) Employing appropriate methods for combining the additives with the AZ91D alloy, such as mechanical stirring, can aid assurance an additional even dispersion.(2) Effective melt processing has facilitated the uniformly-dispersal of additives within the molten AZ91D alloy by controlling temperature and stirring at the appropriate rate.(3) The AZ91D matrix and the additives may interact chemically or physically, making it easier for the additives to be distributed evenly.(4) Under controlled conditions, the additives can be kept from separating and settlement during cooling.
(5) Meticulous assortment of Si 3 N 4 and WGP particle sizes can influence how they disperse within the matrix.Now, the Optical microscopic image (Fig. 16a,b) for AZ91D + 1.5%WGP + 7.5% Si 3 N 4 composites have presented defect-free developed composite after solidification.The α-Mg grains shown by the red background can be detected in optical microscopic images for both "AZ91D + 1.5%WGP + 7.5%Si 3 N 4 ", and "AZ91D + 0%WGP + 9%Si 3 N 4 " fabricated formulated composites.The basal grains own larger sizes and with a smaller spherical second phase.For composition A1, the absence of defects in the developed composites after solidification indicates that the additives were processed and distributed successfully in this composition.This observation is a result of several mechanisms, firstly, before the AZ91D alloy solidifies, Si 3 N 4 and WGP particulates should be thoroughly mixed with it to ensure that the additives are distributed evenly throughout the molten metal.Secondly, the effective wetting among the additives and the molten AZ91D encourages uniform distribution and reduces the formation of flaws or voids.Thirdly, controlled solidification factors, including, cooling rate and thermal gradients, aid in preventing segregation and enable the composite to solidify without significant flaws.Fourthly, the effective incorporation of WGP and Si 3 N 4 without introducing defects can be facilitated by meticulous selection of the particle sizes.
For composition A6, the absence of WGP particulate in this composition indicates that Si 3 N 4 particles within the AZ91D matrix will have a foremost primary microstructure.The absence of WGP is the primary difference between these mechanisms and those considered in the prior composition.
In addition, the grains containing α-magnesium has been identified.Due to their distinctive characteristics, the primary phase of the AZ91D magnesium alloy, the α-Mg grains, can be identified in optical microscopic images.Differences in contrast make it simple to distinguish α-Mg grains in the optical microscope from the surrounding phases.Depending on the orientation of the microscope and the grain structure, the boundaries between α-Mg grains can appear as lines or curves.With the adequate etching methods, it is possible to increase the contrast among α-Mg grains and other phases, making it easier to discover these phases 25,26 .
Furthermore, the larger and lesser spherically symmetrical second-phase of basal grains have been reported.The basal grains (α-Mg grains with a basal plane) in these compositions have greater sizes when compared to a smaller spherical second phase (possibly Si 3 N 4 or another phase), according to optical microscopy 27 .Crystallography and solidification mechanisms can be employed to elucidate the former statement.Firstly, the growth of basal planes is encouraged by the crystal structure of α-Mg, according to crystallography.As a result, the larger grains are inclined toward the basal-grains.Secondly, the second phase, which is moreover compact and spherical, might nucleate and grow differently than the base grains, giving rise to differences in size and morphology.Finally, during solidification environmental circumstances, the cooling rates and thermal gradients can affect the rates at which different phases grow, resulting in changes in grain size [28][29][30] .To increase characteristics, reinforcing particles (such as Si 3 N 4 and WGP particulate) must be properly wettable.For the composition, "AZ91D + 1.5% WGP + 7.5% Si 3 N 4 composites", the findings of the current study demonstrated good-affinity of WGP, and Si 3 N 4 granules with magnesium (Fig. 17a,b).The mechanical behaviour of composite materials is enhanced by adequate wettability.Interfacial adhesion determines wettability.The interfacial adhesion among the AZ91D and reinforcement particles is depicted in Fig. 17a,b.With AZ91D, WGP and Si 3 N 4 particles developed strong bonds, as seen by this interfacial attraction.As wettability is determined by the equilibrium of force among cohesive and adhesive intermolecular contacts, it is the propensity of "reinforcing-constituent particulates" to retain adequate interaction with the surface of matrix-material.Wetting behaviour in metal matrix composites is influenced by a number of variables, including the "density" of the "matrix", and "reinforcing-constituent particulates", "temperature", and "pressure", "time of interaction", "crystallinity", "pathogens", the "surface roughness" of the "reinforcing-constituent particulates", "shape of the reinforcing-constituent particulates", and others.The formation of adequate wettability in the matrix and reinforcement particles, nonetheless, is greatly influenced by the temperature of the reinforcement preheating process.The desorption of moisture/gases, pollutants or decrease of surface impurities, enhanced particle retention, and changed particle surfaces could all result from proper reinforcement preheating 31,32 .Si 3 N 4 addition has a substantial influence on the interfacial layer between Si 3 N 4 and aluminum.One of the main reasons for this is the formation of a reactive Si-Al-O-N layer at the interface, which is formed due to the reaction between the Si 3 N 4 and the aluminum.This layer is crucial to the adhesion between the two materials, and its formation is dependent on the amount of Si 3 N 4 added.Present study has shown that as the amount of Si 3 N 4 added increases, the thickness of the interfacial layer also increases.Moreover, the "thickness of the layer" is directly proportional to the amount of "Si-Al-O-N phase" formed.This suggests that the Si 3 N 4 addition promotes the formation of the Si-Al-O-N phase, which is responsible for improving the adhesion between the two materials.Furthermore, the Si 3 N 4 addition also affects the morphology of the "interfacial-layer".In the absence of Si 3 N 4 , the "interfacial-layer" tends to be discontinuous and irregular.However, the addition of Si 3 N 4 promotes the formation of a smoother and denser layer, which contributes to improved adhesion between the materials 33 .
Moreover, as unveiled from the Fig. 17a-b, the several mechanisms can be employed to elucidate the considerable attraction of Si 3 N 4 and WGP particulate to the magnesium-matrix (AZ91D) in the composite.Firstly, when the additives have a fierce-bonding for the magnesium-matrix, which promotes close contact at the interface, there is appropriate wetting.Surface energies affect wettability because they control how easily a liquid (melted magnesium) spreads over a solid surface (additives).Secondly, the chemical interactions can result in the formation of chemical compounds or robust bonds at the interface among the components of WGP, Si 3 N 4 , and magnesium.For instance, magnesium may react with the oxides in the WGP particulate to form stable compounds.Thirdly during solidification, the melt surrounding the additives may solidify and mechanically fix the particles in spot, escalating their interfacial attraction 33,34 .
Fourthly, the temperature and processing time both contribute to providing enough time for interfacial reactions to take place and for mechanical bonding to form.
Additionally, the interfacial attraction observed in the SEM images indicates that the WGP and Si 3 N 4 particles have a fierce-bonding with the AZ91D matrix.Firstly, the mechanical interlocking, which results in increased bond strength, may be developed as the magnesium matrix solidifies around the additives.Secondly, at the interface, atoms from the additives and the matrix may diffuse, resulting in a diffusion zone with better bonding.Thirdly, the presence of reaction layers at an interface may be an indication of chemical bonding or the synthesis of intermetallic compounds, both of which can strengthen a bond 34,35  www.nature.com/scientificreports/transfer among the additives and the matrix is made possible by a strong interface, which improves load-bearing capacity.An analysis of the Microstructural-morphology of the fabricated AZ91D/WGP/Si 3 N 4 composites have been enumerated.In context with the grain formation is concerned, as evidenced by the micro structures for "AZ91D/WGP/Si 3 N 4 composites" is that the reinforcement's weight-percentages have been evenly-distributed or uniformly-dispersed throughout the AZ91D-matrix.The shape, size, arrangement, as well as dispersion of these grains, that can be evident utilising optical microscopy, have had profound implications on the material's characteristics.An even dispersion of reinforcing-particulates (WGP and Si 3 N 4 ) appeared under the microscope within the AZ91D-matrix, revealing that grain-formation in the composite seemed efficient.In context with the grain structure is concerned, the structure of the grain for a material pertains to the arrangements, structure, and properties of its constituent grains.The optical microscopy images for the "AZ91D-Mg cast-alloy" offer insight into the grain-structure of magnesium (α-Mg).Differences in size of grains, and shape could potentially reveal distinct the process of solidifying circumstances or subsequent processing or post processing techniques.By employing optical microscopic pics, the alpha-Mg grain or particulate structure has been examined.Indicators are the boundaries that separate individual granules, while discrepancies in size and shape may indicate distinct solidification conditions or post-processing techniques.In accordance with the grain refinement is concerned, process of refinement of grains has been accomplished through the inclusion of reinforcing-particulates including WGP and Si 3 N 4 .The incorporation of Si 3 N 4 into the AZ91D-based composites have been reported to substantially raise its mechanical characteristics as well as resistance to wear, demonstrating that it could be contributing to the refinement of grains throughout the AZ91D-MMCs.The microstructural examination revealed that these particulates are evenly-dispersed or uniformly across the AZ91D-matrix, which enhances the material's mechanical characteristics.In context with the phenomenon and mechanisms described for micro structure examination is concerned, a wide spectrum of parameters, including blending techniques, melting processing, interactions between chemicals, and precisely predetermined controlled solidifying circumstances have influenced the microstructure of a material.The SEM images provide insights into the additives' dispersion, while the efficient optimised manufacturing method assures evenly-distribution.The microstructure reveals that the additives are even uniformly-distributed, thus offering substantiation for the manufacturing process's efficiency.This evenly distributed dispersion has been facilitated by mechanisms including suitable blending-techniques, efficient melting-processing, and prospective chemical-interactions.
In accordance with the enhancement of characteristics as a consequence of the grain-fineness process is concerned, the mechanical characteristics, such as hardness, resistance to wear, and tensile strength, are substantially enhanced through the incorporation of WGP and Si 3 N 4 .The phases formed have been examined through microstructural analysis, which comprises of XRD, and SEM analyses.This insight contributes to the enhancement of characteristics.As illustrated by SEM images, the micro structure of the composite has been strengthened as well as uniformly homogenised or dispersed by means of the utilisation of a vacuum-pump.The Halle-Petch connection indicates that a reduction in the size of the grains conduces to a rise in the yield strength of a composite, thus signifying the favourable implications of the refinement of grains on the composite's mechanical characteristics.
In addition, the differentiation among the two reinforcing-particulates (WGP and Si 3 N 4 ) can be identified through an analysis of the subsequent accompanying findings, as for the sample with AZ91D + 1.5%WGP + 7.5% Si 3 N 4 composite is concerned, the morphology for AZ91D matrix waste glass particles and Si 3 N 4 exhibits a nearly uniformly or evenly-dispersal and distributed structure.The SEM images indicate that the WGP, and Si 3 N 4 particulates have been homogenously-dispersed, confirming an efficient blending as well as distribution within the AZ91D-matrix.For sample with AZ91D + 0%WGP + 9% Si 3 N 4 composite is concerned, the predominant presence for Si 3 N 4 in the microstructure signifies that the composition is primarily composed of Si 3 N 4 additive.The Si 3 N 4 particulates were apparently dispersed across the AZ91D-matrix.A dispersion in which processing factors including melting and blending circumstances exert an influence.It has been believed that Si 3 N 4 particulates will eventually get dispersed across the AZ91D-matrix, affecting the structure's microstructure and morphology in a manner that is different from composition AZ91D + 1.5%WGP + 7.5% Si 3 N 4 composite, regardless of the absence of WGP.For sample with AZ91D + 9%WGP + 0% Si 3 N 4 composite is concerned, the micro structure for the AZ91D-matrix comprises primarily of WGP, with particulates apparently dispersed throughout the matrix.The dispersion of WGP particulates throughout the AZ91D-matrix can be impacted by parameters including melting as well as mixing that take place during the manufacturing process.
WGP particulates have been dispersed throughout the AZ91D-matrix.The dispersion has been impacted by factors of manufacturing.The variables which impact dispersion have been elucidated as 36,37 , firstly, the adequate processes for blending additives with AZ91D-matrix has aided a homogeneously-distribution.Then, efficient melting manufacturing controls agitating-speed or stirring-rate, and temperature thus ensuring a homogeneousdistribution.Then, the evenly-dispersion is facilitated by chemical or physical interactions that occur among the AZ91D-matrix as well as additives.Whereas cooling, separation and settlement are prevented by controlled circumstances.Meticulously choice of sizes of particulates including, Si 3 N 4 and WGP has an influence on how they distribute within the AZ91D-matrix.
In general, the SEM images demonstrate that the manufacturing technique effectively incorporated WGP as well as Si 3 N 4 particulates into the AZ91D-matrix in a comparatively uniformly-dispersion. Considerations like suitable blending techniques, efficient melting-processing, probable physical or chemical interactions among the AZ91D-matrix and additives, as well as controlled circumstances throughout processing have all implications for the degree of uniformity or homogeneity of the distribution.
The examination of the microstructure for the composites, as illustrated in Figs.14a-c, 16a,b, and 17a,b reveals significant characteristics.The systematic investigation of the microstructure has comprised an extensivearray of mechanisms as well as phenomena's.Firstly, the performance effectiveness blending and dispersion, by employing appropriate blending techniques and circumstances, WGP, and Si 3 N 4 are uniformly-dispersed throughout the AZ91D-matrix.An optimal pre-heating of reinforcing particulates facilitates proper wettability,   www.nature.com/scientificreports/which in turn enhances intermolecular-interactions between molecules and bonding adhesion-strength 38 .The AZ91D-matrix and additive interactions lead to the reported uniformity of distribution in SEM images.Secondly, the solidification devoid of imperfections or defects or irregularities, as exhibited from the Fig. 16a,b, the Optical microscopy pics for composites that comprised of AZ91D + 1.5%WGP + 7.5%Si 3 N 4 has revealed solidification without any flaws or imperfections.The exemplary performance, efficient functioning, and dispersal of additives throughout this composition are considerations which are responsible for the absence of imperfections.Thirdly, characteristics of the microstructure, as exhibited from the Fig. 16a,b, the α-Mg grain structure is discernible through optical microscopy, exhibiting variations in shape as well as size.Composition A1 has revealed an efficient wettability, controlled-solidification, and precise control of size of particles, as exemplified by an absence of imperfections.Fourthly, the physical and chemical interactions, for an additional evenly homogeneous-distribution, the chemical reactions or physical interactions among reinforcing-particulates, and the AZ91D-matrix have been accountable for it.An optimal efficient stress-transfer or distribution of stress among additives as well as the matrix contributes to a rise in load-bearing performance.Finally, the implications of process operating circumstances, in order to attain uniform dispersion, efficient melting-processing, controlled-temperature, and agitation rates or stirring-speed during manufacturing are extremely significant.Parameters including agitating speed, agitating duration, and wt% proportion formulations of reinforcing-additives exert a profound impact on the morphology.Moreover, the EDS outcomes have been employed to discern the particular phases that have been generated at the interfacial-layer contact among the AZ91D-matrix and Si 3 N 4 and WGP reinforcing-particulates.In this case, as exhibited from Fig. 15, the apparent existence of the respective magnesium peak, silicon peak, aluminium peak, calcium peak, and oxygen peak in the EDS-spectra analysis has revealed conclusive evidence for the inclusion of the corresponding elements throughout the 1.5%WGP/7.5%Si3 N 4 /AZ91D Mg-matrix composites.The occurrence of this most noticeable significant or highest-peak with a spectrum indicates that the magnesium was the primarily predominant element with a particularly higher-concentration, despite various other elements have additionally been detected in varying amounts or proportions.This substantiates the assertion regarding the development of resilient, hard, stable, durable, high strength, tough, corrosion-resistant, resistance against deformation, and robust protective barrier layer composites [36][37][38] .Moreover, the reinforcing-constituents utilised in this investigation is composed of the Si 3 N 4 , and WGP particulates.The EDS findings would provide confirmation that these elements (Si, Ca, Al) have been presented in the developed vacuum stir-casted AZ91D composites.In addition, a uniformly-dispersion, and homogeneity arrangement of Mg, Al, Si, and Ca, elements have indicated the presence of an interfacial-layer among the AZ91D-matrix and Si 3 N 4 along with WGP reinforcing-particulates that is well bonded, homogenous, and evenly-dispersed or arranged in consistency.
The wettability examination, micro structure, and optical examinations for the fabricated composites are displayed in Figs.14a-c, 16a,b, and Fig. 17a,b.The methodical examination involves exploring the underlying mechanisms that are accountable for the observable micro structural characteristics.The resistance to wear is enhanced caused by the evenly distributed distribution of WGP and Si 3 N 4 reinforcing-particulates as shown in the microstructure (Fig. 14a-c).The appearance for defect-free composites in the SEM images (Fig. 17a-b) following the process of solidification indicates that the additives have been effectively dispersed with efficient processing manufacturing method 38,39 .
The optical microscopy analysis of the sample "AZ91D + 1.5%WGP + 7.5%Si 3 N 4 " reveals enhanced characteristics, as demonstrated by the larger α-Mg grain particulates and the reduced dimensions of the sphere-shapedlike second-phase (Fig. 16a,b).The investigation of wettability (Fig. 17a,b) has confirmed that AZ91D-matrix and WGP/Si 3 N 4 reinforcing-particulates have developed strong adhesion bonding-strength, robust resilient-stability, and durability, strength, resulting in strengthening the composite's mechanical characteristics.Parameters such as blending-techniques, melting-processing, and chemical/physical interactions could be attributable for these findings 39,40 .
In the broader scope of the existing research, the wettability study (Fig. 17a,b) and its correlation with interfacial-adhesion and bonding-strength between the surfaces have been examined with particular emphasis on the crucial function of a robust interface in order to strengthen load-bearing performance.The rationale incorporates parameters that impact wettability, including temperature, pre-heating for reinforcement, and the development of reacting-layers at interface-surfaces 40 .This is in accordance with significant academic studies concerning MMC's.
An appropriate distribution of reinforcing-particulates, efficient wettability among additives as well as matrix, and robust interface-adhesion or bonding-strength between surfaces, are considerations that, in accordance with the relevant scientific literature, are contributing to enhanced mechanical characteristics and resistance to wear.The identification of harder phases through XRD analysis, including α-Mg, Si 3 N 4 , and other similar phases, seems to correspond with the existing research that reveals these phases aid to enhanced resistance to wear.
Furthermore, the implications of Si 3 N 4 on interfacial-surfaces layer interaction and the development of Si-Al-O-N phases adheres to scholarly studies that emphasise the vitality of bonding between layers or bonding-strength between surfaces in composites.The implications of WGP reported impacts on fracture toughness, cracking initiation, and propagation correspond with the existing research that explores the impacts of reinforcing characteristics on the performance or behavioural characteristics of composites.Now, in accordance with the phenomenon and mechanism of grain-fineness is concerned, the enhancement of characteristics is primarily attributable to the grain-refinement mechanism, the even distribution of reinforcingparticulates, interface-interaction, and the development of harder-phases [40][41][42] .
In context with the Composite Processing is concerned, the utilisation of the vacuum stir-casting process during composite manufacturing has thereby prevented oxidation, or degradation, or deterioration by ensuring the appropriate or suitable distribution of WGP and Si 3 N 4 reinforcing-particulates.Now, in accordance with the homogenous-distribution is concerned, the microscopic examination corroborated that WGP and Si 3 N 4 were Vol:.(1234567890 www.nature.com/scientificreports/distributed evenly throughout the AZ91D matrix.The grain fineness mechanism primarily depends significantly on this distribution since it promises a consistent homogenous-dispersion of reinforcing-particulates across the composite.Now, in reference with the micro structure enhancement is concerned, the examination of the microstructure evidenced an evenly uniform separation of WGP and Si 3 N 4 , revealing that the manufacturing technique (vacuum stir-casting) adequately achieved homogeneity or uniformity in the composite.Developing homogeneity is a critical indispensable and imperative aspect in the method of the refinement of grains.Now, in accordance with the Wettability and Interface-Bonding is concerned, the SEM images confirmed that the AZ91D matrix, Si 3 N 4 , and WGP particulates have exhibited a superior adhesion, bonding-strength, bindingaffinity, and interfacial-attraction.Efficient wettability, and interfacial-bonding are parameters responsible for contributing to strengthen mechanical strength and load-bearing ability.Now, in context with the mechanical characteristics is concerned, the tensile-strength, hardness, and fatigue-strength of the developed composites were substantially strengthened.The incorporation of Si 3 N 4 and WGP particulates, which possessed optimum suitable wettability, enhanced the work-hardening as well as mechanical characteristics.Now, in reference with the corrosion performance is concerned, the assessment for the resistance to corrosion revealed that the weightloss of the composite was comparatively lesser than that of the AZ91D-matrix.The development of the barrier of oxide shield or protective-layer covering on the surface have contributed to its resistance to corrosion.Now, in context with the tribological behaviour is concerned, the resistance to wear for the composite was significantly enhanced, as evidenced by its reduced rate of wear as well as friction coefficients.Harder phases have been a contributing factor to the raised wear resistance.Finally, in accordance with the XRD analysis is concerned, the presence of harder refractory phases, including α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, and CaO, was observed through the XRD analysis.The aforementioned phases provided substantial contributions to the strengthening of mechanical as well as resistance to wear characteristics.Hence, the enhanced characteristics reported in the composites based on AZ91D-matrix might be ascribed to the grain-fineness mechanism, which includes the development of harder-phases, efficient wettability, and a consistent homogenous-distribution.The combined synergistic effect of inclusion of WGP and Si 3 N 4 particulates, when combined with controlled manufacturing parameters, led to notable enhancements in mechanical characteristics, resistance to wear, and resistance to corrosion.The research underlines the significance of mechanisms concerning grain-refinement in customising the characteristics of magnesium-based composites to suit a broader-spectrum array of applications.

Number of grains with Grain fineness mechanism:
Upon microscopic examination, it became apparent that WGP and Si 3 N 4 were distributed homogeneously across the AZ91D-matrix.It is imperative that these reinforcing-particulates has been evenly-dispersed in order to initiate the grain-refinement process.
The incorporation of 7.5% Si 3 N 4 , and 1.5% WGP particulates has significantly strengthened the material's mechanical characteristics.The enhanced mechanical characteristics can be attributed to the refined structure of the grains.
The process of refinement of grains is accomplished through the modification of the α-Mg sizes of grain-particulates within the AZ91D-matrix.The aforementioned enhancement can be attained by means of the adequate or appropriate distribution of reinforcing-additives, efficient wettability, and the development of harder-phases throughout the fabrication of the composite 42 .
The incorporation of WGP as well as Si 3 N 4 reinforcing-particulates culminated to a rise in tensile strength, demonstrating a positive favorable correlation among the concentration of reinforcing as well as mechanical characteristics.Nevertheless, as the wt% of reinforcing-additives raised, thereby, the ductility has been reduced, underlining the significance of refinement of grains when assessing the composite's performance.
where n = the number of grains, G = grain size number ASTM.
where l α = V vα (L T ) N α .Here V vα = fraction of α phase (volume), L T = length/magnification (test line), N α = grains intercepted (number), Now, Now again G from Eq. ( 2), Now from Eq. ( 1) The examination of a material's microstructure at a 500× magnification has uncovered a significant revelation, shedding light on the intricacies of a composite material comprising AZ91D-alloy, 1.5%WGP, and 7.5%Si 3 N 4 .This detailed analysis has unveiled a precise and noteworthy observations, the material exhibits a remarkable density with 675.58 grains per square inch.The microstructural examination serves as a crucial tool in understanding the composition and properties of materials at a microscopic level.In the case for the AZ91D-alloy composites with WGP and Si 3 N 4 particulates, the higher magnification has allowed for the identification and quantification of individual grains within the material.The specific grain count of 675.58 per square inch not only provides a quantitative measure but also hints at the material's overall structural integrity and potential performance.

Mechanical characteristics of fabricated composites
Tensile strength was reported to be 269.12MPa in the current experiment for the A1 formulated composite sample (Fig. 18a).Results, however, have also demonstrated that the tensile strength for the A6 formulated composite sample has considerably increased with the inclusion of 9-percent of Si3N4.The tensile strength has additionally reduced when WGP wt% in "AZ91D/7.5wt%Si3 N 4 composites" has increased.During tensile testing, the reinforcements with the formulation of developed sample A1, i.e., "(1.5%WGP + 7.5% Si 3 N 4 )" has significantly increase the work-hardening of the composite material.In the AZ91D matrix, this rise in work-hardening is also considerable at "1.5%WGP + 7.5% Si 3 N 4 ".After the incorporation of "reinforcing-constituent particulates" with "1.5%WGP + 7.5% Si 3 N 4 " to the AZ91D-matrix, the composite's tensile strength escalated by 12.13 percent.In addition, the inclusion of "7.5% Si 3 N 4 " as "reinforcing-constituent particulates" to the AZ91D-matrix has raised the composite's tensile strength by 12.68 percent.Figure 18b has summarized the computed hardness values for the various compositions for A1 formulated composite sample.With the escalation in "WGP" up to 1.5% weight percent in "AZ91D/7.5% wt.Si 3 N 4 composites", the hardness of magnesium-alloy has raised.The hardness for the A6 formulated composite sample, however, has exhibited a remarkable outcome, according to the analysis.Figure 18c has depicted the composite material made of magnesium's fatigue strength.The weight-fractions of "reinforcing-constituent particulates" with "1.5%WGP + 7.5% Si 3 N 4 " have a notable impact on fatigue strength.Results revealed that the "1.5%WGP + 7.5% Si 3 N 4 " in the "AZ91D-matrix" has enhanced the fatigue strength by n = 2 (10.40−1) n = 2 (9.40) n = 675.58www.nature.com/scientificreports/roughly 57.84%.The findings reported that by increasing the weight percentage of "WGP", and "Si 3 N 4 ", the ductility of AZ91D was reduced as unveiled from the Fig. 18d.When compared to AZ91D-matrix, the composite material has unveiled lesser plastic deformation as its ductility declines.The ductility of "AZ91D + 1.5%WGP + 7.5% Si 3 N 4 composites" is merely 7.85% lesser than "AZ91D-matrix material".Understandably, the weight percentage of reinforcement, developed porosity, reinforcement features, grain refinement, etc., greatly improved the mechanical properties of composites made of magnesium.Strength, however, primarily depends on grain fineness 42,43 .The microstructure of the composite is thoroughly homogenized and enhanced through building the composite employing the vacuum pump, as seen in the SEM image (Fig. 14a-c).According to the Halle-Petch connection, the composite's yield strength increased as grain size decreased.Second, during tensile deformation, the matrix material is transported together with the reinforcement particles that have the required wettability, improving the mechanical characteristics of the composite.Thirdly, another significant factor that affects the ductility and strength of the Mg-based composites is texture 43 .During the development of a Mg-based composite using waste glass and Si 3 N 4 , the basal texture with Schmidt factor evolved 12 .

Tensile-fractography analysis of developed composites
In accordance with the tensile-fractography examination for the developed composites has demonstrated the brittle fracture failure, including apparent cracks and debonding phenomena, as depicted from the Fig. 19.These findings have offered the significant insights into the failure mechanisms for the fabricated AZ91D composites.As the brittle fractures can be distinguished by the absence of substantial plastic-deformation prior to failure [40][41][42][43] .In AZ91D Mg-alloy, the presence of numerous parameters, including reduced ductility and raised stress-concentration, may eventually lead to the occurrence of brittle fractures characteristic in the developed AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites.In addition, the AZ91D-alloy are highly vulnerable to cleavagefracturing as a consequence of their hexagonally close-packed (HCP) structure of the crystals.When under tension, the planes of cleavage may propagate across the crystal lattice structure which produces fractures that are brittle on the surface of fabricated AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites.The combined effect of stressconcentrations as well as lower-ductility may culminate to the propagation of planes of cleavage throughout the crystal lattice structure.Moreover, the cracks are continuous linear fractures that occur when imperfections or regions with significant stress-concentrations propagate throughout a material.These stress-concentrations have served as a crucial role during the initiation as well as propagation of fracturing-cracks.Cracks can start in locations where stress is concentrated, such as impurities, inclusions, or empty spaces within the AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites.During a tensile test, the application of raising stress has caused cracks to propagate throughout the material, eventually resulting in fracture.The application of tensile-force exacerbates the propagation of these cracks throughout the material.
Additionally, within the AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites, debonding may arise as a consequence of insufficient bonding or adhesion among the matrix (AZ91D) and the reinforcing-phases (WGP, and Si 3 N 4 ).Debonding of materials might occur caused by parameters involving inadequate wetting or the existence of oxides near surfaces.This has a potential to reduce the material's strength, structural integrity and furthermore have an implication on the mechanical characteristics.
Although, the tensile-fractography microstructural examination might potentially reveal the existence of grain boundaries, which function as spots for the initiation of cracks or nucleation.The arrangement, dispersion, structural-layout, and positioning of grains might impact the fracture characteristics of the material.The particulate-agglomeration or clustering has affected the crack trajectory paths.Furthermore, the incorporation of reinforcing-particulates, i.e., WGP, and Si 3 N 4 , could potentially affect the path of cracks, causing crackdeflection or splitting or branched out, which in turn affects the performance or complete fracturing behavioral patterns during tensile-loading.Porosity, if exists, can serve as spots for stress-concentration as well as ultimately www.nature.com/scientificreports/resulting in the initiation, emergence or formation of cracks.Hence, the examination of the tensile-fractured surface of the manufactured composites (AZ91D + WGP + Si 3 N 4 ) unveils indications of brittle fractures, noticeable observable cracks, and debonding.Moreover, the composite comprised of 9% Si 3 N 4 as well as 0% WGP revealed favourable promising findings pertaining to its mechanical, corrosion, and tribological characteristics.The AZ91D Mg-based composites exhibited enhancements in microstructure, durability, resilience, toughness, mechanical-strength, resistance to abrasion, and protection against corrosion as an outcome of the Si 3 N 4 and WGP reinforcing-particulates blend combination.Prospective applications in industries where such superior characteristics are desired have been proposed by the findings.

Corrosion behavior of fabricated composites
In 3.5 weight percent of NaCl corrosive-media for 120 h, the corrosion behaviour of the WGP, and Si 3 N 4 -reinforced AZ91D-based composites has been identified.The weight loss of the sample composition for A1 formulated composite was discovered to be 0.312 mg.Nevertheless, the weight loss for A6 formulated composite sample was found to be 0.294 mg as reported from Fig. 20.Compared to Si 3 N 4 , the presence of silica in waste glass is far more reactive in an acidic environment.However, the development of an oxide surface raises the probability that the surface has reacted with the environment, which has raised the possibility that corrosion has developed [40][41][42][43] .The influence of two key parameters is responsible for the corrosion µresistance and self-effacing resistance of magnesium and magnesium alloys.The high electronegativity of magnesium prevents corrosion when there is an oxygen shortage because cathodic water declines at a negative potential as a counteraction [40][41][42][43] .Due to the hydroxide layers' solubility, the self-effacing shielding characteristic or uniqueness of the films under wet conditions evolved on the surface 13 .MgO is enhanced by the instantaneous interactions of magnesium with oxygen at room temperature.In dry settings, this reaction was seen to occur without any water.The weight-loss for the composite comprised of 0% WGP and 9% Si 3 N 4 within AZ91D-matrix has been reported, and the corrosion-related behaviour of the composite has been assessed under a 3.5% NaCl solution.
As it has been noticed that the reactivity of SiO 2 in WGP particulate in other formulations has been heightened or strengthened when subjected to acidic surroundings.Furthermore, the corrosion characteristics exhibited by the WGP particulate have been impacted by the breakdown of the oxide barrier, protective oxide covering layer, or protective oxide shield when chloride ions have been present.Incorporating both the WGP as well as Si 3 N 4 particulates in combination facilitates the development of a protective shielding oxide-layer; however, the inclusion of chloride ions into the mix accelerates the corrosion process.
The existence of NaCl solution has accelerated the corrosion.Chloride ions have the potential to cause the protective oxide-layer that usually forms on AZ91D-alloy to break down in an aqueous environment.As a result of this breakdown, pits and corrosion products commence to form on the surface and the underlying metal is exposed to the corrosive environment 43 .SEM imaging have illustrated the depressions or craters as the corrosion pits on the sample's surface.SEM images has been employed to analyze and quantify the topography of the pits as well as their size, depth, and dispersion 42,43 .Due to variations in "surface morphology", and "composition", distinct "electron emission" outcomes in the contrast among the pit bottoms and the surrounding material 14,15 .As a consequence of "localized surface attack" brought on by "chemical interactions" with the "corrosive environment", the "corrosion pits" have been developed as exhibited in the Fig. 21a,b.

Tribological behaviour of fabricated composites
The present investigation has examined the wear and friction behaviour of a magnesium-based composite with distinct combinations of "WGP", and "Si 3 N 4 ".Cylindrical pins (Mg-based composite with various mixes of WGP and Si 3 N 4 ) with a height of 10 mm and a diameter of 6 mm were employed for the Pin on Disc testing.Each pin's flat end made touch with the turning disc.The discs were 63 mm in diameter and 6 mm thick, and they were made of cast iron with an average surface roughness of 2 µm and a hardness of 235 HV10.On the basis of the investigation from the pilot-run, the wear-test factors have been selected.The wear and friction behaviour of a "magnesium-based composites" with distinct combinations of "WGP", and "Si 3 N 4 " is shown in Fig. 22a,b.At 5 N loads, 2 m/s sliding speed, and 1000 m of sliding distance, the "wear-rate", and "coefficient of friction" for the developed A1 formulated composite sample were discovered to be 0.0025 mm 3 /m and 0.315, respectively.Findings have indicated that the inclusion of "reinforcing-constituent particulates" with "1.5%WGP + 7.5% Si 3 N 4 " combination has considerably increased the developed composite's resistance to "wear-rate" 16,17 .The enhancement in the "wear-resistance" of the "base-matrix material (AZ91D)" was brought about by the development of hard phases such as "α-Mg", "Al 12 Mg 17 " , "SiO 2 ", "Si 3 N 4 ", "MgO", and "CaO" phases (Fig. 24).
A composite with the formulated-composition of 0% WGP + 9% Si 3 N 4 within AZ91D-matrix composites has been noted for its slight contributions to the enhancement of mechanical characteristics, structural-integrity, and the enhancement of resistance to wear.XRD analysis has revealed an additionally evidence that the inclusion of Si 3 N 4 has contributed to the development of harder-phases [40][41][42] .
All in all, with reference to the formulated composite compositions, a substantial enhancement has been unveiled in the tribomechanical, corrosion and other characteristics upon the incorporation of Si 3 N 4 at an optimal wt% of 7.5% and WGP particulates at 1.5%.
Small particles or debris can be produced during wear processes when the material is subjected to friction and abrasion as evident from the Fig. 23a,b.These granules may break free from the surface and accumulate nearby.These debris fragments has appeared as surface features with irregular forms in SEM images (Fig. 23a,b).
An indication of abrasive-wear may be the existence of profound grooves and debris.As a result of the countersurface's asperities or hard particles cutting into the softer material during abrasive wear, material is removed and grooves are formed [40][41][42][43] .The abrasive wear observed in this instance may be caused by Si 3 N 4 particles or other hard components in the composite 18,19 .The microcracks observed in the Fig. 23a,b point to the occurrence of fatigue or repetitious loading-conditions.Microcracks can commence and spread as a result of "stress concentrations" as the material is subjected to "cyclic-stresses".The WGP particulates may present heterogeneous-regions into the AZ91D-matrix, producing "stress-concentration spots", and promoting the formation of microcracks.
In response to "applied loads", the AZ91D-alloy portion of the composite can deform plastically.The "surface topography" may change and grooves may form as a result of this deformation.

XRD analysis of representative composites
An in-depth understanding of a material's "physical characteristics", "chemical composition", and "crystallographic structure" can be obtained through "X-ray diffraction (XRD) analysis".It is based on a "productive-interference" of a "crystalline specimen", and "monochromatic X-rays".The "XRD behaviour" of produced composite has apparently been observed.The "surface behaviour", "wear", and "mechanical behaviour" of the developed composite are represented by the evolved phases inside the composite 14,15 .Figure 24 has demonstrated that the composite material has the phases "α-Mg", "Al 12 Mg 17 " , "SiO 2 ", "Si 3 N 4 ", "MgO", and "CaO" phases.Peaks that are clearly defined and intense point to a higher degree of crystallinity and to well-ordered atomic arrangements  within the phases.Broader and lesser intense peaks might be a sign of amorphous phases or a decrease in crystallinity 20 .Understanding their atomic arrangements within the composite material is also aided by the evaluation of the crystal-structures of "α-Mg", "Al 12 Mg 17 ", "SiO 2 ", "Si 3 N 4 ", "MgO", and "CaO" phases 43,44 .The role of identified phases through XRD Analysis has been elucidated as follows.Firstly, the crucial primary phase of the AZ91D magnesium alloy is α-Mg.The identification regarding the composite's comprehensive microstructure as well as its mechanical characteristics has been substantially dependent on its presence.Alpha-magnesium grains enhance the strength, durability, resilience, and excellent castability of the composite.When examined through optical microscopy, the particulate size promises significant insight pertaining the circumstances of solidification.The presence of clearly defined distinct peaks associated with the α-Mg phase has been confirmed through XRD analysis, implying a significant degree of crystallinity with properly organized, and structured pattern of atomic-arrangements.An optical microscope illustrates that the existence of larger α-Mg grains has been correlated with a rise in mechanical strength.The material's mechanical characteristics are significantly impacted by the dimensions, arrangement, and dispersion structure layout of α-Mg grains.Variations in methods for post-processing as well as solidifying circumstances may be suggestive of larger grain particulates.Now, the second phase, Aluminium magnesium intermetallic-phase (Al 12 Mg 17 ) is concerned, this intermetallic-phase Al 12 Mg 17 has a capability to impact corrosion's behaviour as well as mechanical characteristics of the composite.The appearance of Al 12 Mg 17 might potentially strengthen the resistance to wear.In order to optimally maximise the positive implications, its dispersion as well as interaction with other phases are, nevertheless, crucial.Now, the third phase Silicon Dioxide (SiO 2 ) is concerned, as SiO 2 is a phase that has been apparently generated from the waste glass particles.It has served as a pivotal contribution in effecting the wear as well as mechanical characteristics of the composite's material.The inclusion of SiO 2 phase within the composite material might strengthen its resistance to abrasive-wear.SiO 2 has the potential to enhance the material's hardness and resistance to wear.In combination with various other phases, its continued existence has influenced the composite's overall resistance to wear, deformation or damage or degradation, deterioration.Now, the fourth phase Silicon Nitride (Si 3 N 4 ) is concerned, as Si 3 N 4 has been incorporated to the composite as a secondary reinforcing material, thereby enhancing its resistance to wear as well as wettability, structural integrity, strengthens the adhesion bonding to the AZ91D-matrix, functionality, resilience, durability, and performance in mechanical terms.Si 3 N 4 has possessed the exceptional mechanical characteristics and is stable under thermodynamic conditions.Its crystalline phases, including beta-Si3N4 and alpha-Si3N4, are contributing to the hardness as well as abrasion resistance of the composite.Numerous crystal structure forms or crystallographic forms, and phases of crystalline structure of Si 3 N 4 (alpha, beta, hexagonal) are contributing towards the composite's general characteristics.It significantly influences the enhancement of mechanical characteristics as well as resistance to wear.Now, the fifth phase Magnesium oxide (MgO) is concerned, as the formation of MgO is generally attributed to the chemical reaction that occurs among magnesium and oxygen during the process of manufacturing or when subjected to the environmental surroundings.MgO phase has potentially strengthened the composite's resistance to corrosion.MgO phase is well-known for its chemically stable characteristics, as well as its elevated melting point.Thermal as well as chemical resistant characteristics for the composite may be impacted by incorporating it in the material.The characteristics of MgO consist of the potential prospective to enhance resistance to corrosion as well as determining the implications of composite's stability in general throughout different environmental circumstances.Now the next phase Calcium oxide (CaO) is concerned, as CaO, which is comparable to MgO, can be generated as a consequence of chemical reactions that occur during the processing stage.It might impact the characteristics of the composite.The resistance to corrosion as well as chemically stable properties for the composite might be influenced by the incorporation of CaO.
Thus, the XRD analysis has confirmed that the synergistic combined blend effect of these phases (α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, and CaO phases) have substantially affected the comprehensive performance and effectiveness of the AZ91D magnesium-based composites.The phases that have been identified correspond with the enhancements in mechanical characteristics, resistance to wear, and corrosion behaviour that were reported in the study's findings.

Desired applications of vacuum stir casted AZ91D + 1.5%WGP + 7.5%Si 3 N 4 composites:
Broader spectrum and potentially influential across numerous industries are engineering applications of AZ91D Mg-MMC's reinforced with Si 3 N 4 and WGP particulates [42][43][44] .Based on the information offered and the findings and characteristics it reveals, the following are several significant applications:

Automotive sector
(1) Weight Reduction Mg-based composites are well-known for their capacity to reduce weight.The mechanical characteristics (raised tensile-strength and resistance to wear) of developed composites have been enhanced through the incorporation of Si 3 N 4 as well as WGP, rendering them well-suited for light-weight automotive parts.This, in turn, leads to enhanced engine performance, energy efficiency, energy savings, vehicle performance, environmental sustainability, fuel efficiency and reduced emissions.(2) Wear Resistance The utilisation of composite materials consisting of 1.5% WGP and 7.5% Si 3 N 4 effectively improves wear resistance.As a result, these materials are well-suited for applications involving components that are susceptible to friction and wear, including engine parts, brake components, and gearbox systems.

Industrial equipment machineries
(1) Components Resistant to Wear The wear resistance exhibited by the composites, especially when 1.5 percent WGP and 7.5 percent Si 3 N 4 are incorporated, rendering them viable materials for abrasive wear-resistant machinery parts, thus prolonging the functional operational service life of such parts.

Electronics and electrical components
(1) Mechanical Strength The strengthened mechanical characteristics of the composites, like, raised tensile strength, modulus, and hardness, render them advantageous in the manufacture of durable electronic and electrical components that require exceptional physicomechanical strength.

Building and construction sector
(1) Structural Components The structural parts are appropriate to such composites as a result of their durability, resilient to mechanical forces, strength, mechanically robust yet light-weight characteristics, providing them appropriate for usage in construction.Application possibilities have comprised of connectors, light-weight panels or boards or sheets, or support structures.

Manufacturing and tooling
(1) Wear-Resistant Equipment The enhanced resistance to wear caused by abrasive agents exhibited by the composite material leads to this well-suited appropriate to be employed in the manufacturing of tools as well as machinery components.This could culminate to raised tool longevity, durability, lifespan, reliability, long-term viability, lifespan sustainability, and reduced maintenance expenses.

Structural components
(1) Superior mechanical characteristics, like toughness, durability, resilience, fracture resistance, tensile strength and hardness, rendering the composites appropriate for usage in structure building frameworks.(2) Corrosion resistance and resistance to wear are desirable characteristics that can be employed in marine settings for shielding or protecting the structural components against environments that are corrosionprone.

Military and defence applications
(1) When reduction in weight tends to be of the nature, magnesium composites possess the potential to be valuable in applications concerning defence and military equipment owing to their light weight as well as their superior durability.
Furthermore, the incorporation of WGP, as well as Si 3 N 4 as reinforcing agents within AZ91D Mg-MMCs offers a spectrum of realistic engineering perspectives characterised by enhanced mechanical, tribological, and corrosion characteristics.The following are several pivotal consideration aspects concerning practical applications as well as significance of the findings:

Enhanced mechanical characteristics
The incorporation of Si 3 N 4 at a weight percentage of 7.5% as well as WGP at a weight percentage of 1.5% has substantially raised the tensile strength of AZ91D magnesium alloy.A rise of 12.13 percent in tensile strength indicates enhanced mechanical performance, resistance to deformation or wear, strength, durability, stability, structural-strength, and functionality.The developed composites have revealed enhanced characteristics in terms of hardness, toughness, durability, strength, fatigue strength, and corrosion resistance.The efficient mechanical characteristics were enhanced through the emergence of hard phases, namely α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, and CaO, which were aided by the blend combination of WGP and Si3N4.
The resistance to wear A substantial reduction in both the wear rate and coefficient of friction was observed in AZ91D composites comprising 1.5% WGP as well as 7.5% Si 3 N 4 , signifying an enhancement in resistance to wear.The existence of wear caused by abrasive debris as well as averting or preventing the occurrence of wear have been both consequences for the existence of harder phases.
The enhanced resistance to wear can be attributable to the development of harder ceramic or refractory phases, which include α-Mg, Al 12 Mg 17 , SiO 2 , Si 3 N 4 , MgO, and CaO.Depending on the material's resistance to microcrack or tiny-fractures formation along with abrasive wear, the composite appeared to be well-suited or ideally appropriated/suitable for applications requiring sliding as well as abrasive contact.
The appearance of micro-cracks or tiny fractures on the worn-surfaces could potentially signify that the composite was subjected to cyclic loading conditions.The long-term performance, reliability, stability, viability, durability, and long-lasting resilience of the reinforcing in the composite can be ascribed to its capacity for withstanding mechanical stresses.

Anti-corrosion characteristics
The corrosion assessment was performed for the composites within a corrosive environment comprising of a 3.5% NaCl solution.In comparison with additional formulation compositions, the weight loss of the composite comprising of 1.5 percent WGP as well as 7.5 percent Si 3 N 4 was lower, exhibiting enhanced resistance to corrosion.
The corrosion of the AZ91D matrix has been mitigated by the development of a protective oxide barrier or shielding layer coating on the surface, which was made more effective or facilitated through the inclusion of Si 3 N 4 and WGP.

Microstructural assessment
The homogeneous evenly dispersal for WGP and Si 3 N 4 in the AZ91D matrix has been demonstrated by microscopic examination, revealing that processing, blending, and dispersion have been carried out efficiently.It is crucial for attaining consistent mechanical characteristics throughout the composite by this uniformly even distribution.
The relatively continuous separation of WGP and Si 3 N 4 particulates reported by the SEM images has indicated that the manufacturing technique was effective in attaining a uniform or evenly dispersion.

Wettability and the adhesion-bonding strength at the interfaces
The findings of the wettability study revealed that the AZ91D matrix as well as the reinforcing particles (WGP and Si 3 N 4 ) developed durable/resilient interfacial bond adhesion strength.The durable interface in concern strengthens both the capacity of bearing loads as well as the overall performance functionality, resilient, efficiency, durability, strength, structural integrity, and mechanical performance.
The formation of chemical bonds or existence of chemicals-interaction has been demonstrated by the emergence of a reactive Si-Al-O-N layered at the interface that exists between Si 3 N 4 as well as AZ91D; this enhanced the adherence bond-strength among the two materials.

Structural analysis
The X-ray diffraction analysis has affirmed the presence of several phases along with provided insightful perceptive comprehension regarding the crystallographic structure, crystallographic arrangement, or the structural of a crystal for the developed composites.A higher degree of crystallinity was apparent by apparent well defined distinct peaks, which contributed to the enhanced mechanical and physical characteristics.
The existence of clearly prominent discernible well defined peaks suggests that the material possesses a substantial level or higher degree of crystallinity or crystalline-structure, along with ordered atomic-arrangements, both of which strengthen the composite material's overall performance.
As an outcome of incorporating Si 3 N 4 and WGP as reinforcement particulates to AZ91D magnesium composites, superior mechanical, tribological, and corrosion characteristics have been accomplished.In automotive components, aerospace structures, and other high-performance engineering applications where raised strength, resistance to wear, and resistance to corrosion are crucial, the synergistic blend combination of these additives possesses real-world applications.

Conclusions
In order to prevent the unfavourable effects of oxidation, this study has utilised recycled WGP, and Si 3 N 4 as reinforcing-particulates within AZ91D Mg-based composites fabricated through vacuum stir casting.The AZ91D-matrix has comprised an evenly-distribution of WGP and Si 3 N 4 reinforcing-additives, as evidenced gate the defects or imperfections in the developed composites.Prospective developments in techniques for manufacturing that are being explored include powder-metallurgy as well as additive manufacturing.(7) Multi-Functional Composites Multifaceted composites have the potential to be manufactured by incorporating additional reinforcement materials or nanoparticles.These composites would exhibit strengthened thermal conductivity, electrical conductivity, or additional desirable characteristics.( 8) Nanostructured Additives This investigation seeks at examining the potential possibilities or applications of nanostructured additives, specifically Si 3 N 4 as well as WGP, to significantly enhance the distribution characteristics within the AZ91D-matrix along with subsequently strengthen its mechanical characteristics.(9) Multi-Scale Modeling Multi-scale modelling ought to be adopted in order to simulate the composite's behaviour or performance activity across various length scales or dimensions.This will give researchers an additionally comprehensive understanding concerning the material's thermal as well as mechanical characteristics.(10) Statistical analysis and Computational Modelling Develop computational mathematical models that simulate the composite's performance under varying loading-conditions; this will aid in the optimisation as well as prediction of mechanical characteristics.In addition, the incorporation of statistical analysis or mathematical modelling to further validate the reliability for the findings along with derive additional robust outcomes concerning the scope of the reported enhancements.(11) Life Cycle Assessment (LCA) To aid in the development of sustainable materials, perform a LCA technique aimed at assessing the adverse environmental consequences for both the manufacturing and disposal of such composites.( 12) Advanced Characterization Techniques By employing advanced methods for characterization, including in-situ measurements, it can be accomplished to record instantaneous real time variations within the material as it undergoes mechanical testing or is subjected to the surrounding environment.
By contemplating such aspects, the further research studies and subsequent investigations may expand upon the present investigation while offering a valuable contribution to the progressive development of magnesiumbased composites throughout a broader spectrum array variety of applications.

Limitations of the present study
Although substantial advanced findings and progressive developments have been accomplished in the present research, it is nevertheless essential to understand the following limitations: (1) Analysis of a Single Composition The investigation was confined to a particular set of compositions; subsequent studies ought to take into account a broader spectrum array of compositions in order to ascertain the material's versatility or resilience.

Figure 20 .
Figure 20.Corrosion weight loss of the developed composites with distinct formulations.

Figure 22 .
Figure 22.(a) Wear behavior, (b) Friction behavior of the developed composites with distinct formulations.

( 2 )
Environmental Implications An exhaustive evaluation regarding the environmental consequences, involving the consumption of energy throughout the manufacturing process along with final or eventual end-oflife disposal considerations, has been absent from the study.(3)Simplified Corrosion-environmental Limitation The corrosion activity was examined within a specified environment comprising 3.5% NaCl.The response to additional corrosive circumstances necessitates additional research.(4) Theoretical Modeling The investigation has limitations in theoretical mathematical or computational model frameworks that make predictions regarding the behaviour that was observed.Additional investigations are appropriate to take into account conceptual frameworks or mathematical-models in order to shed light on testing outcomes.https://doi.org/10.1038/s41598-024-52804-y

Table 1 .
Chemical constituents of the cast alloy of magnesium AZ91D.

Table 2 .
Mechanical characteristics of AZ91D magnesium cast alloy.

Table 4 .
Stir casting parameters for the developed AZ91D MMCs.

Table 5 .
Composition formulations of developed composites.
Weight savings In the aviation sector, magnesium composites are significant paramount for minimising the total weight of aircraft as a result of their light weight.Steel brackets, housings, and structural components, underlying support structures or foundation part elements are instances of components whose mechanical characteristics have the potential to be enhanced.(2)Resistance to Corrosion Material resistance to corrosion is a crucial requirement or vital requirement in aviation applications as a result of numerous environmental conditions which materials have been subjected towards Scientific Reports | (2024) 14:3217 | https://doi.org/10.1038/s41598-024-52804-ywww.nature.com/scientificreports/(1)